BESTPOLUX PCTM-1
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VGmaDk_BESTPOLUX-PCTM-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/PETnatural lubrified with impact modified to gain improvements in injection and moulding generally used for pieces in conjunction with improved dimesional stability, better impact and good final surface with good HDT temperature for general industry. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 15 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress | 59.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 132 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+16 | ohms | IEC 60093 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 275 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Urochem 136 | Chemiplastica, Inc. | Urea Formald | Urochem |
| ATPioneers PP CAP502 | Asia Technology Pioneers Ltd | TPO | ATPioneers PP |
| Fainplast PVC RK 317/UV | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Duratron® T4503 | Quadrant Engineering Plastic Products | PAI | Duratron® |
| TOTAL Polypropylene PPH 3485WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |