VENYL SFRHWGT300H - 8229
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VGVQG8_VENYL-SFRHWGT300H---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SFRHWGT300H - 8229 is a 30% glass fibre/mineral reinforced polyamide 6 (UL 94 V2 at 1,6 mm) intended for Injection moulding. APPLICATIONS VENYL SFRHWGT300H - 8229 has been developed especially for very demanding applications in automotive industry where fire resistance is needed. VENYL SFRHWGT300H - 8229 is available in black but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8400 | 6900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | 88.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 6100 | 5000 | MPa | ISO 178 |
| Flexural Stress | 142 | 130 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 34 | 40 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 3.20 mm | HB | -- | ||
| 1.60 mm | V-2 | -- |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Horizontal Flame Test 1 | B | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 240 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 245 to 270 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Test Method: D45 1333 (PSA norm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 A1VS01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Sindustris PC GP5201 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Bakelite® UP 3620 | Hexion Inc. | Polyester, TS | Bakelite® |
| Arak HDPE BL6 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| LUVOCOM® 80-7713-NA | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |