Innothane® IE-80A
| Category: | TSU-Ether , Polyurethane Thermoset Elastomer, Polyether Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VGEDxo_Innothane-IE-80A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-80A is a semi-flexible polyurethane elastomer formulated for hand-batch or vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.04 | g/cm³ | |
| Cured | 1.09 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 35 Mix Ratio by Volume: 30 | ||
| Demold Time | 240 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 0.98 | Pa·s | |
| 25°C 3 | 1.5 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 7.0 to 13 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 11.7 | MPa | ASTM D638 |
| Tensile Elongation at Break | 250 | % | ASTM D638 |
| Tear Strength | 31.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2712CC | NOVA Chemicals | HDPE | SCLAIR® |
| SCANAMID 6 B12^ F25 FR6 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| TECHNYL® A 218W V30 BLACK FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| KW Plastics KWR102 | KW Plastics | HDPE | KW Plastics |
| Karina CLEAR PVC COMPOUND 833-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |