Zenite® ZE55311E
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Zenite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VFgPuW_Zenite-ZE55311E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zenite ZE55311E is mineral filled LCP resin with improved elongation, low abrasion and smooth surface. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.73 | % | ISO 294-4 |
| Flow direction | 0.050 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 4.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 258 | °C | ISO 75-2/A |
| Melting Temperature 1 | 320 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (2.05 GHz) | 4.27 | IPC TM-650 2.5.5.13 | |
| Dissipation Factor (2.05 GHz) | 1.4E-3 | IPC TM-650 2.5.5.13 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 335 - 345 | °C | |
| Front Temperature | 335 - 345 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 325 - 345 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 335 to 345°CFeed Temperature: 40 to 60°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4985A | Teknor Apex Company | TPE | Telcar® |
| Smooth-Cast® 300Q | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| FHR EPS 55-6455 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Gallonprene® GP100-8002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Generic PPE+PS+Nylon - Glass Fiber | Generic | PPE+PS+Nylon | Generic |