ADENE NHJA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A.D. Compound spa |
| Trademark: | ADENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VFW5Dg_ADENE-NHJA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADENE NHJA is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% talc. It is available in Europe or North America. Primary attribute of ADENE NHJA: Homopolymer. Typical application of ADENE NHJA: Consumer Goods |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Ash Content | 30 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 11 | % | |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 9.5 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ NT-818.G002-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| WPP PP PPC3TF2-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| NatureFlex™ 45NVR | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| HiFill® PC GF20 X | Techmer Engineered Solutions | PC | HiFill® |
| LinGen FR350 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | LinGen |