NILAMID® XS3 GF30
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VFPySs_NILAMIDXS3GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
SPECIALTY PARTIALLY AROMATIC POLYAMIDE BLEND
PARTIALLY AROMATIC PA, 30% GLASS FIBER REINFORCED |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.60 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.15 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | ISO 62 |
| Saturated, 23°C | 4.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | 8300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 170 | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | 4.1 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.7 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 8.6 | 9.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 58 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 70 | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.5 | 9.5 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 195 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 3 | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | HB | -- | UL 94 | |
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SAP-3300E30 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| AKROMID® B3 ICF 20 1 L black (5296) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Gallonprene® GP310-6503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LIHAN® T703 | Nanjing Lihan Chemical Co., Ltd. | PBT | LIHAN® |
| TOTAL Polypropylene PPR 12236 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |