SABIC® PPcompound 7450
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VEnCoZ_SABICPPcompound7450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 7450 is a mineral filled, impact modified polypropylene TPO. This material can exhibit high impact resistance and good paintability in automotive exterior applications. The IMDS is 87784390. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.968 | g/cm³ | ASTM D792 |
| -- | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 80°C, 1 hour | 1.2 | % | Internal method |
| Vertical flow direction : 23°C, 48 hours | 1.0 | % | Internal method |
| Flow direction : 80°C, 1 hour | 0.74 | % | Internal method |
| Flow direction : 23°C, 48 hours | 0.69 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1130 | MPa | ASTM D638 |
| -- | 1370 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 15.0 | MPa | ASTM D638 |
| Yield | 18.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 13.0 | MPa | ASTM D638 |
| Fracture | 13.9 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 9.0 | % | ASTM D638 |
| Yield | 4.1 | % | ISO 527-2/50 |
| Fracture 5 | 300 | % | ASTM D638 |
| Fracture | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1100 | MPa | ASTM D790 |
| 64.0mm span 7 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 4.9 | kJ/m² | ISO 179/1eA |
| 23°C 9 | No Break | ISO 179/1eA | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 10 | 450 | J/m | ASTM D256 |
| -30°C 11 | 5.6 | kJ/m² | ISO 180/1A |
| 0°C 12 | No Break | ISO 180/1A | |
| 23°C 13 | No Break | ISO 180/1A | |
| Unnotched Izod Impact 14(23°C, 3.20 mm) | 980 | J/m | ASTM D4812 |
| Instrumented Dart Impact 15 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 20.9 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 14.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 79.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed 16 | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.20mm | 49.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 17 | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/A50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 210 - 270 | °C | |
| Nozzle Temperature | 210 - 270 | °C | |
| Processing (Melt) Temp | 210 - 270 | °C | |
| Mold Temperature | 15.0 - 60.0 | °C | |
| Back Pressure | 1.00 - 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 63.5*12.7*3.2mm, Cut |
| 11 . | 80*10*4mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 80*10*4mm, Cut |
| 14 . | 63.5*12.7*3.2mm, Cut |
| 15 . | 2.20 m/sec |
| 16 . | 80*10*4mm, Cut |
| 17 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A33^E | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Braskem PP R7022-50NA | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| API PS 505 | American Polymers, Inc. | PS (HIPS) | API PS |
| Diaterm® B26 GF25 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 66 | Diaterm® |
| Petrothene® NA960083 | LyondellBasell Industries | LDPE | Petrothene® |