Exelene® HDPE 54050M

Category:	HDPE, HMW , High Density (HMW) Polyethylene
Manufacturer:	Montachem International, Inc.
Trademark:	Exelene® HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VEcGh9_Exelene-HDPE-54050M.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Applications:

55 gallon plastic drums, chemical tanks for agriculture, automobile gasoline tanks.

Characteristics:

The Exelene resin HDPE 54050M meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Features	Copolymer Food Contact Acceptable High Density High Molecular Weight
Uses	Agricultural Applications Automotive Applications Drums Food Service Applications Fuel Tanks Non-specific Food Applications
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Extrusion Blow Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.954	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) ¹(190°C/21.6 kg)	5.5	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
50°C, 3.10 mm, 100% Igepal CO-630, F50	> 200	hr	ASTM D1693A
50°C, 1.90 mm, 100% Igepal CO-630, F50	> 200	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, 23°C)	68		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - Tangent ²(3.20 mm)	1310	MPa	ASTM D638
Tensile Strength ³(Yield)	28.3	MPa	ASTM D638
Tensile Elongation ⁴(Break)	600	%	ASTM D638

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.20 mm)	670	J/m	ASTM D256A
Tensile Impact Strength	189	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ⁵(0.45 MPa, Unannealed)	78.0	°C	ASTM D648
Brittleness Temperature ⁶	< -75.0	°C	ASTM D746A
Vicat Softening Temperature	126	°C	ASTM D1525 ⁷
Melting Temperature	263	°C	DSC

Note Message
1 .	HLMFI
2 .	13 mm/min
3 .	Type IV, 50 mm/min
4 .	Type IV, 50 mm/min
5 .	2°C/min
6 .	F50; 25 lbf*in
7 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
PRE-ELEC® TPE 1502	Premix Oy	TPE	PRE-ELEC®
Sup-tech P364	Shanghai Suptech Engineering Plastics Co. Ltd.	PP, Unspecified	Sup-tech
TEREZ PMMA 5605 SZ	TER HELL PLASTIC GMBH	Acrylic (PMMA)	TEREZ PMMA
ADDILENE PMD 50215	ADDIPLAST	PP Copolymer	ADDILENE
Edgetek™ AT-1000	PolyOne Corporation	Acetal (POM) Copolymer	Edgetek™