Polytron® P50B01
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VEFakI_Polytron-P50B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A chemically coupled 50% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.30 | % | |
| -- | 0.20 to 0.30 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 135 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 210 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 27 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 250 | J/m | ASTM D256 |
| 23°C | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 159 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 167 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 20 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 4060 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| NILAMID® A3 GF30 TF15 | Nilit Plastics | Nylon 66 | NILAMID® |
| alphalon™ 32 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| EPO-TEK® T7109-19 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Heraflex® A 57-41-90 | Radici Plastics | SEBS | Heraflex® |