Cevian®-V SKG20
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VE7SGn_Cevian--V-SKG20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V SKG20 is an Acrylonitrile Butadiene Styrene (ABS) material filled with 20% glass fiber. It is available in Asia Pacific. Primary attribute of Cevian®-V SKG20: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 90.0 | MPa | ISO 527-2 |
| Flexural Modulus | 7100 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C | |
| Ball Pressure Test | 95 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 22 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | PLC 7 | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADMER™ AT2539E | Mitsui Chemicals Europe GmbH | MDPE | ADMER™ |
| Complet® LBF50-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| CP PRYME® Nylon 66 NN233HSL BK | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| LNP™ LUBRICOMP™ MX06404 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |
| POLYabs R00 | Polykemi AB | ABS | POLYabs |