Monprene® CP-29353 NAT XRD1 (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VDZKQB_MonpreneCP29353NATXRD1PRELIMINARYDATA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®CP-29353 NAT XRD1 (PRELIMINARY DATA) is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Monprene®The main features of CP-29353 NAT XRD1 (PRELIMINARY DATA) are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 45 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 55 | ASTM D2240 | |
| Shaw A, 5 seconds | 53 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| Transverse flow : 100% strain | 1.72 | MPa | ASTM D412 |
| Flow : 100% strain | 3.14 | MPa | ASTM D412 |
| Transverse flow : 300% strain | 2.90 | MPa | ASTM D412 |
| Flow : 300% strain | 4.38 | MPa | ASTM D412 |
| Tensile Strength 2 | ASTM D412 | ||
| Transverse flow : Fracture | 5.88 | MPa | ASTM D412 |
| Flow : Fracture | 5.65 | MPa | ASTM D412 |
| Tensile Elongation 3 | ASTM D412 | ||
| Transverse flow : Fracture | 690 | % | ASTM D412 |
| Flow : Fracture | 540 | % | ASTM D412 |
| Tear Strength 4 | ASTM D624 | ||
| Transverse flow | 32.0 | kN/m | ASTM D624 |
| Flow | 24.9 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr | 77 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 127 - 149 | °C | |
| Middle Temperature | 138 - 160 | °C | |
| Front Temperature | 149 - 171 | °C | |
| Nozzle Temperature | 171 - 193 | °C | |
| Processing (Melt) Temp | 171 - 193 | °C | |
| Mold Temperature | 16 - 32 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | C mold, 510mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® PLUS PLS93G35DH1 BK261 | DuPont Performance Polymers | Nylon 6 | Zytel® PLUS |
| CompaDur® 121 GF 10 natural (003) | DimeLika Plast GmbH | PBT | CompaDur® |
| Daelim Po1y® PR-770B | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Kalix® 2930 HFFR | Solvay Specialty Polymers | HPPA | Kalix® |
| Karina GRAY PVC COMPOUND 881-18/501-E-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |