Ecovio® F23B1
| Category: | Copolyester , Copolyester |
| Manufacturer: | BASF Corporation |
| Trademark: | Ecovio® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VDXdU4_EcovioF23B1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ecovio® F23B1 is our biodegradable product containing renewable resources. It is basically a compound of our biodegradable, statistical, aliphatic-aromatic copolyester ecoflex® and a small amount of polylactic acid (PLA). Due to its outstanding mechanical strength ecovio® F23B1 offers a great down gauging potential needed for very thin film applications like T-shirt bags, organic waste bags etc. ecovio® F23B1 already contains antiblocking and slip agents required for easy processing on film extrusion and film conversion equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 - 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 5.00 - 11.0 | cm³/10min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 260 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 130 | MPa | ISO 527-3 |
| Tensile Strength | ISO 527-3 | ||
| MD : 25 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 480 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 570 | % | ISO 527-3 |
| Dart Drop Impact (25 µm, Blown Film) | 250 | g | ASTM D1709A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm, blown film | 1.3 | N | ISO 6383-2 |
| TD : 25 µm, blown film | 0.90 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | DSC | ||
| -- 1 | 110 - 120 | °C | DSC |
| -- 2 | 140 - 155 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | ecoflex® |
| 2 . | PLA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 1035 04 F | ROMIRA GmbH | PC+ABS | Romiloy® |
| Primefin V500TL40HS | Lucent Polymers, Inc. | PP Homopolymer | Primefin |
| RAMSTER PF300G3 | Polyram Ram-On Industries | PBT | RAMSTER |
| Huafon JF-P-8065 / JF-I-8815 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Polifor® TR/30 H-D-R NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |