Viton® A-100
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DuPont Performance Elastomers |
| Trademark: | Viton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VDGHp1_Viton-A-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Viton A-100 fluoroelastomer is an ultralow-viscosity, "A-type" gum polymer that demonstrates improved processing and rheology in comparison with existing fluoroelastomers. Viton A-100 is especially designed for use with Viton Curative #50. It may be blended with other Viton types to enhance flow and processibility. Compared with other "A-family" dipolymers, Viton A-100 provides: -Ultralow viscosity -Improved processing -increased mold flow -can be blended with other Viton types to enhance processibility and improve flow -Excellent mold release -Good compression set resistance for low-viscosity types of Viton Applications -Transfer and injection molding of complex shapes such as gaskets -Extrusions --can be used to modify viscosity of other types of Viton -Solution coating --fabric --tanks or chemical containers |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | ASTM D792 |
| Mooney Viscosity (ML 1+10, 121°C) | 33 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 79 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 3.80 | MPa | ASTM D412 |
| Tensile Strength (Break) | 8.20 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 240 | % | ASTM D412 |
| Compression Set | |||
| 23°C, 70 hr | 10 | % | ASTM D395B |
| 200°C, 70 hr | 21 | % | ASTM D395 |
| 232°C, 22 hr | 23 | % | ASTM D395B |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| 200°C, 70 hr | 43 | % | ASTM D573 |
| 100% strain, 200°C, 70 hr | 110 | % | ASTM D573 |
| 200°C, 168 hr | 45 | % | ASTM D573 |
| 100% strain, 200°C, 168 hr | 100 | % | ASTM D573 |
| 232°C, 24 hr | 30 | % | ASTM D573 |
| 100% strain, 232°C, 24 hr | 45 | % | ASTM D573 |
| 232°C, 70 hr | 41 | % | ASTM D573 |
| 100% strain, 232°C, 70 hr | 110 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | ASTM D573 | ||
| 200°C, 70 hr | -36 | % | ASTM D573 |
| 200°C, 168 hr | -35 | % | ASTM D573 |
| 232°C, 24 hr | -24 | % | ASTM D573 |
| 232°C, 70 hr | -37 | % | ASTM D573 |
| Change in Durometer Hardness in Air | ASTM D573 | ||
| Support a, 200°C, 70 hr | 1.0 | ASTM D573 | |
| Support a, 200°C, 168 hr | 2.0 | ASTM D573 | |
| Support a, 232°C, 24 hr | 4.0 | ASTM D573 | |
| Support a, 232°C, 70 hr | 4.0 | ASTM D573 |
| Additional Information |
|---|
| Mooney Scorch, MS at 121°C, Minimum: 17 in-lbMooney Scorch, MS at 121°C, 2-pt rise: >30 minODR at 177°C, Microdie, 3° Arc, 15 min, ML: 2 in-lbODR at 177°C, Microdie, 3° Arc, 15 min, ts2: 2.7 minODR at 177°C, Microdie, 3° Arc, 15 min, tc90: 4.1 minODR at 177°C, Microdie, 3° Arc, 15 min, Mc90: 83 in-lbODR at 177°C, Microdie, 3° Arc, 15 min, MH: 92 in-lbRosand Capillary Rheometer, 100°C, 1.5 mm Die, L/D=0/1, 12.7 mm/min, 113 s^-1: 4.0 MPaRosand Capillary Rheometer, 100°C, 1.5 mm Die, L/D=0/1, 50.8 mm/min, 452 s^-1: 6.8 MPaRosand Capillary Rheometer, 100°C, 1.5 mm Die, L/D=0/1, 127 mm/min, 1130 s^-1: 9.9 MPaNominal Viscosity, ML 1 + 10, 121°C: 10Polymer Fluorine Content: 66% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP WPP311D | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Fainplast PVC PG 56/B | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Haysite SMC 54500 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| Hostacom X M2 T20 | LyondellBasell Industries | PP Copolymer | Hostacom |
| AURUM® JCF3030 | Mitsui Chemicals, Inc. | PI, TP | AURUM® |