Honeywell PCTFE P800TR

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell PCTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VD4dSz_Honeywell-PCTFE-P800TR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Honeywell PCTFE P-Series TR film is a poly-chlor-tri-fluoroethylene homopolymer, high performance barrier film for industrial and electronics applications. It provides outstanding water vapor barrier and excellent chemical resistance.

General Information
Features	Good chemical resistance Barrier resin
Uses	Films
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.07	g/cm³	ASTM D792

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1030	MPa	ASTM D882
TD	896	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	58.6	MPa	ASTM D882
TD : Fracture	34.5	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	200	%	ASTM D882
TD : Fracture	250	%	ASTM D882
Water Vapor Transmission	0.78	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	195	°C	ASTM D3418

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	100	%	ASTM D2863

Optical	Nominal Value	Unit	Test Method
Haze	< 0.50	%	ASTM D1003

Additional Information
Yield: 17777 in²/lbTensile Strength @ Break, ASTM D 882, MD: 7000 to 10000 psiTensile Strength @ Break, ASTM D 882, TD: 4000 to 6000 psiElongation @ Break, ASTM 882, MD: 150 to 250%Elongation @ Break, ASTM 882, TD: 200 to 300%Secant Modulus, ASTM D 882, MD: 140000 to 160000 psiSecant Modulus, ASTM D 882, TD: 120000 to 140000 psiGraves Tear (initial), ASTM D 1004, MD: 300 to 350 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -12 to -15% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +12 to +15% shrinkageFlammability: Non-flammable

Additional Information

Yield: 17777 in²/lbTensile Strength @ Break, ASTM D 882, MD: 7000 to 10000 psiTensile Strength @ Break, ASTM D 882, TD: 4000 to 6000 psiElongation @ Break, ASTM 882, MD: 150 to 250%Elongation @ Break, ASTM 882, TD: 200 to 300%Secant Modulus, ASTM D 882, MD: 140000 to 160000 psiSecant Modulus, ASTM D 882, TD: 120000 to 140000 psiGraves Tear (initial), ASTM D 1004, MD: 300 to 350 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -12 to -15% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +12 to +15% shrinkageFlammability: Non-flammable

Resin Grade	Manufacturer	Category	Trademark
Susteel® G-10	TOSOH Corporation	PPS	Susteel®
TIPPLEN® H 543 F	MOL Petrochemicals Co. Ltd.	PP Homopolymer	TIPPLEN®
VAMPSAB 023 V0	Vamp Tech	ABS	VAMPSAB
3M™ Dyneon™ Fluoroelastomer FC 2176Z	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer
Hyflon® AD 40L	Solvay Specialty Polymers	Perfluoropolymer	Hyflon® AD