Supol H-700

Category:	TPO (POE) , Thermoplastic Polyolefin Elastomer
Manufacturer:	Shanghai Suptech Engineering Plastics Co. Ltd.
Trademark:	Supol
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VC4qto_Supol-H-700.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
H-700 by reactive extrusion into the legal system of maleic anhydride grafted elastomer copolymer of ethylene and octene copolymer ( POE ) , substrate selection . H-700 has a low gel, grafting ratio, light in color, which is widely used in engineering plastics ( PA6 , PA66 , PBT , etc.) of toughening modification; also can be used as a compatibilizer to improve the glass fiber, fillers and the compatibility of the matrix resin; and greatly improve the adhesion between the resin or resin metal in the multi-layer co-extruded. Typical applications PA6 , PA66 , PBT , and other engineering plastics flexibilizer of glass fiber reinforced and fill the PA of PBT do compatibilizer to improve the interface compatibility performance PA / PP alloy compatibility agent Bond performance of the multi-layer co-extruded film resin layer between the resin between the metal

Message

H-700 by reactive extrusion into the legal system of maleic anhydride grafted elastomer copolymer of ethylene and octene copolymer ( POE ) , substrate selection . H-700 has a low gel, grafting ratio, light in color, which is widely used in engineering plastics ( PA6 , PA66 , PBT , etc.) of toughening modification; also can be used as a compatibilizer to improve the glass fiber, fillers and the compatibility of the matrix resin; and greatly improve the adhesion between the resin or resin metal in the multi-layer co-extruded.

Typical applications

PA6 , PA66 , PBT , and other engineering plastics flexibilizer

of glass fiber reinforced and fill the PA of PBT do compatibilizer to improve the interface compatibility performance

PA / PP alloy compatibility agent

Bond performance of the multi-layer co-extruded film resin layer between the resin between the metal

General Information
Features	Copolymer Good Adhesion Low Gel Octene Comonomer
Uses	Bonding Film Plastics Modification
Processing Method	Coextrusion Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.890	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/10.0 kg)	4.0	g/10 min	ASTM D1238
MAH Graft Level	Gao

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness	95		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	10.0	MPa	ASTM D638
Tensile Elongation (Break)	500	%	ASTM D638
Flexural Modulus	220	MPa	ASTM D790A

Resin Grade	Manufacturer	Category	Trademark
TECHNO MUH C7103	Techno Polymer Co, Ltd.	ABS	TECHNO MUH
Stamylex® 2H 568	Borealis AG	LLDPE	Stamylex®
Vydyne® 47H NT	Ascend Performance Materials Operations LLC	Nylon 66	Vydyne®
Karina SILVER PVC COMPOUND -E 808-47/ 14-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
MAJORIS EEX850	AD majoris	PP, Unspecified	MAJORIS