SLOVALEN® PC 46 FRD 3 T 35
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VAc5Ox_SLOVALEN-PC-46-FRD-3-T-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified copolymer PP for injection moulding, with the content of 35 % microground chemically modified talc, retarded with halogen flame retardant. Application - electrical industry - terminals, coil forms, covers of electrotools, guides. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.60 | % | |
| Water Content | 0.10 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 1.8 | kJ/m² | |
| 23°C | 3.8 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 16 | kJ/m² | |
| 23°C | 34 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 73.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 175 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 48 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C | |
| Injection Pressure | 70.0 to 90.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 MF UV BRCA011 PC318 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Makrolon® RW6267 X | Covestro - Polycarbonates | PC | Makrolon® |
| XENOY™ HX6600HP resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| apifive® 3010-350 | API SpA | Polyolefin, Unspecified | apifive® |
| Fainplast PVC PG 6016/1 | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |