DuraStar™ DS2010
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | DuraStar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VAaX67_DuraStar-DS2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Durastar™ DS2010 polymer contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. DS2010 has very good toughness as shown by Izod impact resistance. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS2010 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily and fills intricate molds. Under existing United States Food and Drug Administration (FDA) regulations, Durastar™ DS2010 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240. This product is certified to ANSI/NSF Standard 51. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| 23°C | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 46.0 | MPa | ASTM D638 |
| Yield, 23°C | 47.0 | MPa | ISO 527-2 |
| Break, 23°C | 53.0 | MPa | ASTM D638 |
| Break, 23°C | 49.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 310 | % | ASTM D638 |
| Break, 23°C | 210 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1900 | MPa | ASTM D790 |
| 23°C | 1750 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 64.0 | MPa | ISO 178 |
| Yield, 23°C | 67.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 60 | J/m | ASTM D256 |
| 23°C | 370 | J/m | ASTM D256 |
| -40°C | 6.3 | kJ/m² | ISO 180 |
| 23°C | 30 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | |||
| -40°C, Energy at Peak Load | 48.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 45.0 | J | ASTM D3763 |
| -40°C, Energy to Peak Force | 55.0 | J | ISO 6603-2 |
| 23°C, Energy to Peak Force | 71.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 73.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(23°C) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 23°C, 1 kHz | 2.60 | ||
| 23°C, 10 kHz | 2.60 | ||
| 23°C, 100 kHz | 2.50 | ||
| 23°C, 1 MHz | 2.50 | ||
| Dissipation Factor | ASTM D150 | ||
| 23°C, 1 kHz | 6.0E-3 | ||
| 23°C, 10 kHz | 0.012 | ||
| 23°C, 100 kHz | 0.015 | ||
| 23°C, 1 MHz | 0.015 | ||
| Arc Resistance | 123 | sec | ASTM D495 |
| Comparative Tracking Index | 700 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm, AT) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | ASTM D1003 | ||
| Total | 91.0 | % | |
| Regular | 89.0 | % | |
| Haze | 0.30 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang WU-6100RP | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| Vinylbond 6527P-MD Grey 499 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Baydur® 641 IBS (20 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Arak LLDPE HD5218EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| DENILEN B 5010 CB | Vamp Tech | PP, Unspecified | DENILEN |