Stat-Tech™ AS-10CF/000 Black
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VAGc6b_Stat-Tech-AS-10CF-000-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.040 to 0.20 | % | |
| Across Flow | 0.20 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5720 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1.2 | % | ASTM D638 |
| Flexural Modulus | 6620 | MPa | ASTM D790 |
| Flexural Strength | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 48 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 97.8 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 91.7 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+6 | ohms·cm | ASTM D257 |
| Static Decay - (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | 2 | msec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 227 to 238 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® AER003N | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| Silopren® LSR 2610 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| ExxonMobil™ PP1014H1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Grilon® TSG-30/4 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| POLYFLAM® RPP 3225 GW | A. Schulman Europe | PP Homopolymer | POLYFLAM® |