Compound based on Polyamide 66 (PA 66). Heat stabilised. Toughened. Glass fibres. Very good impact resistance. Good flexibility even at low temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 0.55 to 0.85 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 4600 | MPa | |
| 60°C | 3700 | MPa | |
| 90°C | 2100 | MPa | |
| 120°C | 1700 | MPa | |
| 150°C | 1500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 100 | MPa | |
| Yield, 60°C | 70.0 | MPa | |
| Yield, 90°C | 55.0 | MPa | |
| Yield, 120°C | 45.0 | MPa | |
| Yield, 150°C | 40.0 | MPa | |
| Break, 23°C | 100 | MPa | |
| Break, 60°C | 70.0 | MPa | |
| Break, 90°C | 50.0 | MPa | |
| Break, 120°C | 45.0 | MPa | |
| Break, 150°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.0 | % | |
| Yield, 60°C | 4.0 | % | |
| Yield, 90°C | 8.0 | % | |
| Yield, 120°C | 8.0 | % | |
| Yield, 150°C | 7.0 | % | |
| Break, 23°C | 4.0 | % | |
| Break, 60°C | 7.0 | % | |
| Break, 90°C | 12 | % | |
| Break, 120°C | 12 | % | |
| Break, 150°C | 10 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 55 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -20°C, 3.20 mm | 45 | J/m | |
| 23°C, 3.20 mm | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | |
| Vicat Softening Temperature | 235 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 153 SP30 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Radiflam® A RV500 AF 375 NER 4849 | Radici Plastics | Nylon 66 | Radiflam® |
| Hanwha Total PP TB52U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Hostacom G3 U01 L | LyondellBasell Industries | PP Homopolymer | Hostacom |
| HOPELEN JC-160 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |