COSMOPLENE® AX161S
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V9cgLl_COSMOPLENEAX161S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE AX161S is a high impact PP copolymer manufactured by the latest gas phase process licensed from Sumitomo Chemical Co. Japan. It exhibits good impact and stiffness balance at high melt flow rate. COSMOPLENE AX161S also shows excellent flowability and good surface appearance of parts after molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 2.00mm | 1.5 | % | Internal method |
| Transverse flow : 2.00mm | 1.7 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 27.0 | MPa | ASTM D638 |
| Fracture | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 37 | J/m | ASTM D256 |
| 23°C | 93 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Mold Temperature | 30 | °C | |
| Injection Pressure | 6.86 | MPa | |
| Clamp Tonnage | 0.98 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2207 HF | RTP Company | PEEK | RTP |
| REPLEX 0805 R BLK | Buckeye Polymers, Inc. | ABS | REPLEX |
| Staramide RF003S | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| SIBUR Synthetic Rubber NBR 1855 | SIBUR | NBR | SIBUR Synthetic Rubber |
| LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |