Ateva® 1880A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V939k9_Ateva-1880A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for hot melt coating and adhesive applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (125°C/0.325 kg) | 500 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 4.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 570 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 31.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 78.0 | °C | ASTM D3418 |
| Ring and Ball Softening Point | 89 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T & T Marketing TT 130 FR | T & T Marketing, Inc. | TP, Unspecified | T & T Marketing |
| Thermoset Plastics 211 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Vikalloy P84 | Viking Polymers, LLC | PMMA+PVC | Vikalloy |
| Chiao Fu PA66 MD212G13 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| DuraFlex 403-2 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |