Pinnacle PP 1525
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Pinnacle Polymers |
| Trademark: | Pinnacle PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V8okZ8_Pinnacle-PP-1525.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
25 MELT FLOW HOMOPOLYMER FOR FIBER SPINNING Pinnacle Polymers Polypropylene 1525 is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for fiber spinning and other critical extrusion applications. The 1525 product provides:
Pinnacle's polypropylene, as marketed by Pinnacle Polymers, in natural, uncolored pellet form complies with appropriate requirements of CFR Title 21, Part 177, Subpart B, Section 177.1520 (c) 1.1a entitled "Olefin Polymers" of the Food Additives Amendment of 1958 to the United States Food, Drug and Cosmetic Act of 1938. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 34.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, 3.20 mm, Injection Molded) | 9.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(3.20 mm, Injection Molded) | 1620 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 3.20 mm, Injection Molded) | 27 | J/m | ASTM D256 |
| Notched Izod Impact (Area) 5(23°C, 3.20 mm, Injection Molded) | 2.60 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 108 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 1.3 mm/min |
| 4 . | Type I |
| 5 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 218L V30 BLACK Z/4 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| VALOX™ 732E resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Generic PVC, Semi-Rigid | Generic | PVC, Semi-Rigid | Generic |
| HANWHA LLDPE 3322 | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| PERLER® N09H4001B00 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |