Lucky Enpla LKH
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V8A3uZ_Lucky-Enpla-LKH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LKH is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: automotive industry. The main characteristics are: heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 49.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2550 | MPa | ASTM D790 |
| Flexural Strength 3 | 79.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| 3.18 mm | 230 | J/m | ASTM D256 |
| 6.35 mm | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 101 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 220 - 240 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 1.96 - 3.92 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 220-230°CInjection Pressure (1st Pressure): 700-1200 kg/cm²Injection Pressure (2nd Pressure): 400-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PE 1011.LDH | Guangdong Silver Age Sci & Tech. Co., Ltd | LLDPE | SILVER® |
| TOTAL Polyethylene HDPE 2008 SN 60 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Formolene® 2510W | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LUVOCOM® 1104-VAP 10 | Lehmann & Voss & Co. | PEK | LUVOCOM® |
| LNP™ LUBRICOMP™ DL001 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |