DIAMALOY ENGINEERED ALLOYS PC/PBT 627
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ENGINEERED ALLOYS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V7pl10_DIAMALOY-ENGINEERED-ALLOYS-PC-PBT-627.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIAMALOY ENGINEERED ALLOYS PC/PBT 627 is a Polycarbonate + PBT (PC+PBT) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(260°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (Injection Molded) | 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | < 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2000 | MPa | ASTM D790B |
| Flexural Strength 4(Yield) | 75.8 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 800 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 86.7 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 121 | °C | |
| Drying Time - Desiccant Dryer | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Melt Temperature (Aim) | 271 | °C | |
| Mold Temperature | 54.4 to 82.2 | °C | |
| Injection Pressure | 55.2 to 96.5 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 0.345 to 0.517 | MPa | |
| Back Pressure | 0.552 to 1.03 | MPa | |
| Screw Speed | 50 to 75 | rpm | |
| Clamp Tonnage | 4.1 to 6.9 | kN/cm² | |
| Cushion | 2.54 to 7.62 | mm |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Method I (3 point load), 1.3 mm/min |
| 4 . | Method I (3 point load), 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T40P100-01A | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| STYRON™ 678E | Trinseo | PS (GPPS) | STYRON™ |
| APEX® 3603-75NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Exxtral™ Performance Polyolefin CMU236 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Sylvin 9302-70 FUV WHITE 1337 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |