Rotec® PC 7015
| Category: | PC , Polycarbonate |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V6xtmG_Rotec-PC-7015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rotec® PC 7015 is a Polycarbonate (PC) material. It is available in Europe for injection molding. Primary attribute of Rotec® PC 7015: Flame Rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 62.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTAMID™ MB3ZUV | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| Chemlon® 133 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| LUVOCOM® 19-8073 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| 3M™ Dyneon™ Fluoroelastomer FE 5522 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| LNP™ LUBRICOMP™ JX91198 compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |