Halene H E5201S
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V6aAiG_Halene-H-E5201S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
E5201S is a broad molecular weight distribution HDPE, produced by the Mitsui CX Process. The Grade is used for General Purpose Blow Molding Applications. It can also be used for Double Walled Corrugated Pipes & General Purpose Pipe Applications E5201S combines exceptional processability and excellent mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | 200 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molding | 36.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, molding | 11 | % | ASTM D638 |
| Fracture, molding | > 600 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 150 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Die Temperature | 160 - 165 | °C |
| Extrusion instructions |
|---|
| Parison Temperature: 165 to 170°CCooling Water for Mold: 20 to 25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech A707GH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| Sylvin 8349-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Viton® GF-600S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| DEXFLEX® 727 | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| 3M™ Dyneon™ PTFE Compound TF 6712 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |