Order Products : sales@su-jiao.com
Daplen™ EF210AE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V6RCmr_Daplen-EF210AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EF210AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. Applications: Daplen EF210AE has been developed especially for the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.65 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 300 | % | ISO 527-2 |
| Flexural Modulus 2 | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.5 | kJ/m² | ISO 179/1eA |
| 23°C | 60 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 50 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/A |
| CLTE - Flow 3 | 4.5E-5 | cm/cm/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Temperature: Low to MediumFlow Front Speed: 100-200 m/min |
| Note Message | |
|---|---|
| 1 . | disk |
| 2 . | 2.0 mm/min |
| 3 . | -30°C/80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTARIN® H AF | Röchling Sustaplast SE & Co. KG | Acetal (POM) Homopolymer | SUSTARIN® |
| Taitalac® 1000 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Trexlink™ 4770 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Forprene® 6NM001D40 | SO.F.TER. SPA | TPV | Forprene® |
| Elastron® D D100.A58.N | Elastron USA, Inc. | SBS | Elastron® D |