Cereplast Compostables® 5001
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Compostables® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V5yKnd_Cereplast-Compostables-5001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 5001, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 5001 has been designed to have an excellent balance of strength, toughness and processability. Compostable 5001 can be processed on existing extrusion machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. Compostable 5001 is recommended for foam extrusion of sheets which can be thermoformed in meat trays, plates, egg cartons, clamshells and more… |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength (Break) | 55.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 92.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 47.8 | °C | ASTM D648 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Cylinder Zone 1 Temp. | 171 | °C | |
| Cylinder Zone 2 Temp. | 182 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 4 Temp. | 188 | °C | |
| Cylinder Zone 5 Temp. | 188 | °C | |
| Adapter Temperature | 188 | °C | |
| Melt Temperature | 188 | °C |
| Extrusion instructions |
|---|
| Speed: (RPM) 57.2Head Pressure: (PSI) 1090Amperage 84 (100 max)Feeder Talc: (TPM 1823) 1 lbs/hourGas Setting: (Isobutane) 8 lbs/hourLine Rate: 220 pounds/hour |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP256 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| TYNEC® 1100 | Tyne Plastics LLC. | PC | TYNEC® |
| Grivory® HTV-4H1 black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Ducor® 1104K | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| Eleme NGH045IU | Eleme Petrochemical Company Ltd | HDPE | Eleme |