Plenco 00755 (Injection)
| Category: | Mel Phenolic , Melamine Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V5N0Nc_Plenco-00755-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 00755 is a melamine-phenolic copolymer molding compound offering excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 00755 is available only in brown. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Apparent Density | 0.57 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.76 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.36 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 73 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10400 | MPa | ASTM D638 |
| Tensile Strength | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.90 | % | ASTM D638 |
| Flexural Modulus | 8640 | MPa | ASTM D790 |
| Flexural Strength | 89.4 | MPa | ASTM D790 |
| Compressive Strength | 161 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20.2 | J/m | ASTM D256 |
| Notched Izod Impact | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 177 | °C | ASTM D648 |
| Continuous Use Temperature | 151 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 7.7 | kV/mm | ASTM D149 |
| -- 2 | 5.0 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 7.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.078 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 525 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 240hr, 105°C: 1.06%Heat Resistance, ASTM D794: 151°CDrop Ball Impact, PLENCO Method: 118 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 150 - 177 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HF | RTP Company | PP Homopolymer | RTP |
| Tufpet PBT G2630 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| BJB Polyurethane F-82 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Flextuff® S2850-00 | Noble Polymers | TPE | Flextuff® |
| MAXATEL® AH100ST-BK | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |