4TECH® 9S22120
| Category: | Polyphenylene, Unspecified , Polyphenylene |
| Manufacturer: | 4Plas |
| Trademark: | 4TECH® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V4cg9d_4TECH-9S22120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4TECH 9S22120 is a Standard Flow 20% Glass Fibre Reinforced PPO |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 11 | kJ/m² | ISO 180/1A |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | 250 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E95 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| DOMAMID® A1-002-V15-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Hostacom TRC 411Y | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LNP™ LUBRICOMP™ RX05495 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Sylvin 4200-65 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |