Sarlink® TPV 4139D
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V43I9N_Sarlink-TPV-4139D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SARLINK® 4000 series are high hardness, multi-purpose thermoplastic elastomers with excellent flex fatigue resistance, heat resistance, improved elasticity and resilience designed primarily for demanding automotive applications. SARLINK® 4139DN can be processed by injection molding, extrusion and blow molding to produce clamps, grommets, profiles, boots, bellows and ducts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.948 | g/cm³ | ASTM D792 |
| -- | 0.950 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw D, 5 seconds, extruded | 39 | ASTM D2240, ISO 868 | |
| Shore D, 5 seconds, injection molding | 40 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Transverse flow : 100% strain | 8.89 | MPa | ASTM D412 |
| Flow : 100% strain | 13.3 | MPa | ASTM D412, ISO 37 |
| Transverse flow : 100% strain | 8.90 | MPa | ISO 37 |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 19.0 | MPa | ASTM D412, ISO 37 |
| Flow : Fracture | 18.0 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 700 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 420 | % | ASTM D412, ISO 37 |
| Tear Strength | |||
| Transverse flow | 96.3 | kN/m | ASTM D624 |
| Flow 1 | 97 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 46 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 56 | % | ASTM D395, ISO 815 |
| 125°C, 70 hr | 80 | % | ASTM D395, ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -15 | % | ASTM D573, ISO 188 |
| 100% strain, 135°C, 1000 hr | 20 | % | ASTM D573 |
| 150°C, 168 hr | -15 | % | ASTM D573, ISO 188 |
| 100% strain, 150°C, 168 hr | 15 | % | ASTM D573 |
| 100% strain 135°C, 1000 hr | 20 | % | ISO 188 |
| 100% strain 150°C, 168 hr | 15 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -20 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | -20 | % | ASTM D573, ISO 188 |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Support d, 135°C, 1000 hr | 2.0 | ASTM D573, ISO 188 | |
| Support d, 150°C, 168 hr | 2.0 | ASTM D573, ISO 188 | |
| Change in Volume | |||
| 125°C, 70 hr, in IRM 903 oil | 47 | % | ASTM D471 |
| 125°C, 70 hr, in IRM 903 oil | 47 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 100 | °C | UL 746 |
| RTI | 100 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm, All Colors) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 370 | Pa·s | ISO 11443 |
| 200°C | 370 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 185 - 220 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 204 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 188 - 210 | °C | |
| Melt Temperature | 193 - 216 | °C | |
| Die Temperature | 193 - 216 | °C | |
| Take-Off Roll | 21.1 - 48.9 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshCompression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badalac® ABS 20 GF15 | Bada AG | ABS | Badalac® |
| Dyna-Purge® X | Dyna-Purge, division of Shuman Plastics | Proprietary | Dyna-Purge® |
| Lumid® SG4389B | LG Chem Ltd. | Nylon 66 | Lumid® |
| Eleme JPRG030 | Eleme Petrochemical Company Ltd | PP Homopolymer | Eleme |
| Sylvin 6231-90 White 1587 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |