TORZEN® U4630HSL BKB01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V3hl35_TORZEN-U4630HSL-BKB01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® U4630HSL BKB01 is a heat-stabilized, lubricated molding grade PA66 in black color. The heat stabilizer system has been designed to provide excellent property retention in high temperature applications. U4630HSL is also available in natural color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.3 | % | |
| Flow : 2.00 mm | 2.4 | % | |
| Water Absorption (23°C, 24 hr) | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.2 | % | |
| Break | 30 | % | |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.6 | kJ/m² | |
| 23°C | 5.3 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 5.7 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Melting Temperature | 265 | °C | ISO 11357-3 |
| CLTE | ASTM E831 | ||
| Flow : 23 to 55°C, 2.00 mm | 8.7E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 8.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (2.00 mm) | 10 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.710 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.710 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 750 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Screw Speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Silicone TC-5060 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| APEX® RE 8207 OB | Teknor Apex Company | PVC, Rigid | APEX® |
| Glastic® CBC-NBC | Glastic Corporation | Polyester, TS | Glastic® |
| PERLER® O07U1000B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| PENTALLOY BTA H UV black 9040 | PENTAC Polymer GmbH | PBT+ASA | PENTALLOY BTA |