ADMER™ QF551E
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Mitsui Chemicals Europe GmbH |
| Trademark: | ADMER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V342k9_ADMER-QF551E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ADMER® QF551E is a maleic anhydride grafted, co-PP based grade for strong bonding between PP and EVOH, PA or Aluminum, and is therefore suitable for highperformance applications in blown film, composite pipe, injection molding or coating process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 17.0 | MPa | |
| Break | 17.0 | MPa | |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (Area) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Peak Melting Temperature | 147 | °C | ASTM D3418 |
| Oxidation Induction Time (210°C) | 7.0 | min | ISO 11357-6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RESPOND™ EX4290 | LyondellBasell Industries | Polyolefin, Unspecified | RESPOND™ |
| CP PRYME® ABS A230G | Chase Plastics Services Inc. | ABS | CP PRYME® ABS |
| Ebalta GM 976 / PUR 1 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| KOPA® KN173ST | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| ProPolymers PPA TI-35G | ProPolymers Inc. | PPA | ProPolymers |