DOWLEX™ 2038.68G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V2xhWs_DOWLEX-2038-68G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance (25 µm) | 7.69 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 25 µm | 97.5 | J/cm³ | ASTM D882 |
| TD : 25 µm | 115 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm | 377 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm | 348 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 15.2 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 16.7 | MPa | ASTM D882 |
| MD : Break, 25 µm | 38.3 | MPa | ASTM D882 |
| TD : Break, 25 µm | 33.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 520 | % | ASTM D882 |
| TD : Break, 25 µm | 660 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 71 | g | ASTM D1922 |
| TD : 25 µm | 410 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 126 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 58 | ASTM D2457 | |
| Haze (25.4 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 246 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：单跨，双混合 模具间隙：70 密尔 (1.8 mm) 熔体温度：400-475°F (200-250°C) 输出：模具周长的 7 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：87.3 rpm 冷冻线高度：23 英寸 (584 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ LDF-0220B | Muehlstein | LDPE | CERTENE™ |
| LNP™ THERMOCOMP™ IF003 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| POLYFORT® FPP 1068 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| SCHULAMID® 66 GF 30 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sylvin 9077-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |