LNP™ THERMOCOMP™ MF006SXP compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V2ZEsW_LNP-THERMOCOMP-MF006SXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* MF006SXP is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled. Also known as: LNP* THERMOCOMP* Compound MFX-1006 Product reorder name: MF006SXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.96 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7310 | MPa | ASTM D638 |
| -- | 7600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 88.1 | MPa | ASTM D638 |
| Break | 91.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6210 | MPa | ASTM D790 |
| -- | 8700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 139 | MPa | ASTM D790 |
| -- | 159 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 3 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.70 | J | ASTM D3763 |
| -- | 2.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 151 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 152 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN ST900 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| NuSil EPM-2461 | NuSil Technology | Silicone | NuSil |
| BMC 304 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Fiberfil® M-2271 NAT | Fiberfil® Engineered Plastics Inc. | Nylon 6 | Fiberfil® |
| Electrafil® PC 05004 FR | Techmer Engineered Solutions | PC | Electrafil® |