LNP™ LUBRICOMP™ EX00548C compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V2KBNT_LNP-LUBRICOMP-EX00548C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* EX00548C is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Clean Compounding System, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-E-00548 CCS Product reorder name: EX00548C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.66 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.22 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3030 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 85.4 | MPa | ASTM D638 |
| Yield | 86.0 | MPa | ISO 527-2 |
| Break | 83.7 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.1 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2 |
| Break | 8.1 | % | ASTM D638 |
| Break | 7.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 3390 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 149 | MPa | ASTM D790 |
| -- | 143 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 2 | 4.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 470 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 4.90 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 185 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 184 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 TFE 5 | RTP Company | Nylon 66 | RTP |
| TECHLEN DM411 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Geon™ Vinyl Flexible C8009 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 8200-88 Brown 7453 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 86032-90 Clear 8443 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |