Braskem PE HS4506A
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V1Zpkn_BraskemPEHS4506A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HS4506A is a High Density Polyethylene specially developed for the manufacturing of blow molding fuel tanks. It has high molar mass and shows excellent processability. Besides, it shows excellent tenacity, high resistance to stress cracking, and outstanding impact resistance. The resin contains additives to protect it against ultraviolet radiation action. Application: Mono and multilayer fuel tanks for trucks; sheet extrusion for pickup rear protectors. Process: Blow Molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 5.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 24.0 | MPa | ASTM D638 |
| Fracture, molding | 38.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 11 | % | ASTM D638 |
| Fracture, molding | 1600 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 62.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M6113 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| FLEXAREN® 07000 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| FORMULA P ELAN 6003 UV | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Infino FD-1112 | SAMSUNG SDI CO., LTD. | PC | Infino |
| Sylvin 5175-92 Green 3154 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |