Petrotene® PP B3 T40 HS NTLA013 PH343
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V1MBVu_Petrotene-PP-B3-T40-HS-NTLA013-PH343.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer natural color, talc filler, 40% filler by weight, thermally stabilized. Resistant to oil, grease and many solvents, good set of mechanical properties and excellent dimensional stability. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Ash Content | 37 to 43 | % | ASTM D2584 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 52 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 20.0 | MPa | |
| Break | 17.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 15 | % | |
| Flexural Modulus | 1700 | MPa | ASTM D790 |
| Flexural Strength | 26.0 to 29.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 115 | °C | |
| 1.8 MPa, Unannealed | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 246M BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| NYLOY® MG-0013N | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Clariant Nylon 6/6 PA-133G13 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LUVOCOM® 1200-8835 | Lehmann & Voss & Co. | ABS | LUVOCOM® |
| LEXAN™ LUX7189 resin | SABIC Innovative Plastics | PC | LEXAN™ |