NYCOA Polyamide 5300 HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V0ME9K_NYCOA-Polyamide-5300-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 5300 HS is a heat stabilized, super tough Nylon 66 which offers outstanding toughness, exceptional processability, and a greater service life at elevated temperatures than standard grades of Nylon 66. NYCOA 5300 HS is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. NYCOA 5300 HS is found in applications such as chain saw casings, ski bindings, and lawn & garden equipment housings. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 48.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 75 | % | ASTM D638 |
| Flexural Modulus 3 | 1600 | MPa | ASTM D790 |
| Flexural Strength 4 | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 189 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| Melting Temperature | 258 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 249 - 266 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 288 | °C | |
| Processing (Melt) Temp | 277 - 293 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Evolue™ SP2520H | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| FRIANYL® B3 H V0 | Nilit Plastics | Nylon 6 | FRIANYL® |
| ENFLEX S3125A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Hifax TRC 779X | LyondellBasell Industries | TPO (POE) | Hifax |
| Kalix® 9950 | Solvay Specialty Polymers | HPPA | Kalix® |