Leona™ 90G50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uzn7Mt_Leona-90G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 90G50 is a Polyamide 66 (Nylon 66) product filled with 50% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 90G50 include automotive, engineering/industrial parts, fabrics/fibers and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.58 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.2 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.2 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ||||
| M-Scale | 90 | -- | ASTM D785 | |
| R-Scale | 120 | -- | ASTM D785, ISO 2039-2 | |
| M-Scale | 100 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 18000 | 17000 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 250 | 200 | MPa | ISO 527-2 |
| -- | 235 | 196 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.5 | 3.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 15500 | 12100 | MPa | ASTM D790 |
| 23°C | 14200 | 12000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 373 | 304 | MPa | ASTM D790 |
| 23°C | 355 | 239 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 16 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 88 | 84 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | 130 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 240 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | -- | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PA 1408 | Premix Oy | Nylon 6 | PRE-ELEC® |
| Ranger PBT PBT-201-G0 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Network Polymers PP PPB 25 1316 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Ducor® DE1040U | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| Elastollan® R 3001 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |