LNP™ STAT-KON™ QD000I compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UziHPt_LNPSTATKONQD000Icompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound Q-HI Product reorder name: QD000I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.28 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 31.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 53 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 54.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 55.0 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+4 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ E 205S | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| LNP™ LUBRICOMP™ MG004 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ LUBRICOMP™ |
| Eleme NGC500I | Eleme Petrochemical Company Ltd | PP Impact Copolymer | Eleme |
| Sylvin 8375-87C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® CP-15150D-10 NAT XRD1 | Teknor Apex Company | TPE | Monprene® |