Generic PP, Unspecified - Mineral
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UypGbE_Generic-PP-Unspecified---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.996 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 0.955 - 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 3.5 - 21 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 1.0 - 31 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 7.85 - 18.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.60 - 1.5 | % | ASTM D955 |
| Transverse flow : 23°C | 1.3 | % | ASTM D955 |
| 23°C | 0.46 - 1.4 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 - 0.031 | % | ASTM D570 |
| 23°C, 24 hr | 0.030 - 0.10 | % | ISO 62 |
| Equilibrium, 23°C | 0.020 - 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 52 - 108 | ASTM D785 | |
| 23°C | 90 - 98 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 54 - 74 | ASTM D2240 | |
| 23°C | 60 - 71 | ISO 868 | |
| Ball Indentation Hardness | 25.6 - 81.1 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1830 - 5170 | MPa | ASTM D638 |
| 23°C | 1140 - 3140 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 16.9 - 35.1 | MPa | ASTM D638 |
| Yield, 23°C | 13.4 - 33.5 | MPa | ISO 527-2 |
| Fracture, 23°C | 12.0 - 48.3 | MPa | ASTM D638 |
| Fracture, 23°C | 10.4 - 32.4 | MPa | ISO 527-2 |
| 23°C | 16.5 - 31.1 | MPa | ASTM D638 |
| 23°C | 19.0 - 30.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 4.0 - 10 | % | ASTM D638 |
| Yield, 23°C | 2.8 - 8.2 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 61 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 110 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1120 - 2860 | MPa | ASTM D790 |
| 23°C | 1020 - 3030 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 24.1 - 81.0 | MPa | ASTM D790 |
| 23°C | 19.8 - 57.8 | MPa | ISO 178 |
| Yield, 23°C | 33.2 - 47.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 - 37 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 18 - 110 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 21 - 66 | J/m | ASTM D256 |
| 23°C | 2.0 - 51 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 37 - 530 | J/m | ASTM D256 |
| 23°C | 14 - 72 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 14.9 - 31.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 92.5 - 156 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 89.3 - 132 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 51.5 - 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 46.8 - 77.3 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 97.5 - 155 | °C | ASTM D1525 |
| -- | 36.0 - 156 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 160 - 182 | °C | |
| -- | 165 - 166 | °C | ISO 3146 |
| CLTE - Flow | |||
| -- | 4.4E-5 - 1.0E-4 | cm/cm/°C | ASTM D696 |
| -- | 6.0E-6 - 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 65.0 - 112 | °C | UL 746 |
| RTI Imp | 65.0 - 120 | °C | UL 746 |
| RTI | 65.0 - 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 - 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| 23°C | 19 - 40 | kV/mm | ASTM D149 |
| 23°C | 19 - 43 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C) | 2.0E-3 - 2.1E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 743 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 23 - 28 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.0 - 80.0 | °C | |
| Drying Time | 2.0 - 3.5 | hr | |
| Suggested Max Moisture | 0.010 - 0.015 | % | |
| Suggested Max Regrind | 15 | % | |
| Hopper Temperature | 59.8 - 60.0 | °C | |
| Rear Temperature | 199 - 200 | °C | |
| Middle Temperature | 215 - 216 | °C | |
| Front Temperature | 215 - 216 | °C | |
| Nozzle Temperature | 220 - 221 | °C | |
| Processing (Melt) Temp | 209 - 241 | °C | |
| Mold Temperature | 39.4 - 50.8 | °C | |
| Injection Pressure | 74.2 - 87.6 | MPa | |
| Holding Pressure | 44.7 - 46.1 | MPa | |
| Back Pressure | 0.345 - 44.1 | MPa | |
| Screw Speed | 45 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO F-3740 | Prime Polymer Co., Ltd. | PP Random Copolymer | PRIME TPO |
| Versaflex™ 9570-1 | PolyOne Corporation | TPE | Versaflex™ |
| Xuchuan 2000/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| DESOX™ DSC640M5 | DESCO Co., Ltd. | PBT+PET | DESOX™ |
| OnForce™ LFT NN-50LGF/001 HS X2 WHITE UV | PolyOne Corporation | Nylon 66 | OnForce™ LFT |