Compound based on Polyoximethylene (POM). UV stabilised. Toughened. Low viscosity. Very high toughness properties and impact resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.3 to 2.7 | % | |
| Flow : 2.00 mm | 2.3 to 2.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2700 | MPa | |
| 60°C | 1400 | MPa | |
| 90°C | 800 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 45.0 | MPa | |
| Yield, 60°C | 30.0 | MPa | |
| Yield, 90°C | 20.0 | MPa | |
| Break, 23°C | 40.0 | MPa | |
| Tensile Strain (Break, 23°C) | 90 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 65.0 | °C | |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 175 to 200 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S USX270 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Witcom PC/ABS AS-S-LM | Witcom Engineering Plastics B.V. | PC+ABS | Witcom PC/ABS |
| Geon™ Vinyl Rigid Molding M3800 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| KumhoSunny PPO HPP8340 | Shanghai KumhoSunny Plastics Co., Ltd. | PPE+PS | KumhoSunny PPO |
| Infino NH-1230U | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |