Badamid® PPA GF30 H FR HF
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uy755c_BadamidPPAGF30HFRHF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Heat stabilized injection moulding grade based on a partially aromatic Polyphtalamid; Halogen and red phosphorous free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 215 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 2.4 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 313 | °C | ISO 3146 |
| Linear thermal expansion coefficient | DIN 53752 | ||
| Flow | 3.0E-5 | cm/cm/°C | DIN 53752 |
| Lateral | 7.0E-5 | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 60216 | ||
| -- | 270 | °C | IEC 60216 |
| -- 5 | 160 | °C | IEC 60216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | V-0 | UL 94 | |
| 1.6 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.8 to 1.6mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 320 - 340 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/min |
| 5 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT C213 GF15 FR | Polykemi AB | PBT+PET | POLYshine |
| POYAD VM111 | Pooya Polymer Tehran | PP, Unspecified | POYAD |
| MORETEC™ 0248Z | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| Daplen™ ED306UBB | Borealis AG | TPO | Daplen™ |
| Grivory® XE 4134 black 9225 | EMS-GRIVORY | Nylon 10T/X | Grivory® |