Sindustris PBT GP2307FY
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UxsQdG_Sindustris-PBT-GP2307FY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT GP2307FY is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PBT GP2307FY are:
Typical application of Sindustris PBT GP2307FY: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 9810 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 205 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 215 | °C | |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+19 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 28 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 250 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 245 to 255 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-20H | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| 4DUR® 9K22130 XHFR1 | 4Plas | PBT | 4DUR® |
| Hostacom M2 U02 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LinGen FR195 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPE | LinGen |
| OTECH PVC OW134 - Wire Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |