MAJORIS DFR111R
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uxl3U0_MAJORIS-DFR111R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR111R is a PP flame retardant compound with UL 94 V2 classification, intended for injection moulding. The product is available in natural (DFR111R) but other colours can be supplied on request. DFR111R produces very low level of toxicity and low smoke density in the case of a fire. DFR111R is halogen free following norm DIN VDE 0472 Part 815. APPLICATIONS DFR111R is intended for the injection moulding of electrical component such as:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.4 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 200 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 68.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | IEC 60695-2-13 |
| 2.00 mm | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tuf-Stif 2804 | Axiall Corporation | PVC, Rigid | Tuf-Stif |
| AIE ABS 20G3 | Asia International Enterprise (Hong Kong) Limited | ABS | AIE ABS |
| Sylvin 8225-80 Brown 7428 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8200-88 Red 648 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9915-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |