AKROMID® A3 1 L natural (4800)
| Category: | Nylon 66+PP , Polyamide 66 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uwuai5_AKROMID-A3-1-L-natural-4800-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 1 L natural (4800) is a unreinforced and heat stabilised polyamide-blend with a reduced density compared to standard PA66 Applications are mainly technical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 65.0 | MPa | |
| -- | 80.0 | MPa | |
| Flexural Strain at Break 4 | 7.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Melting Temperature 5 | 262 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 6(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Standard Flexural Stress |
| 4 . | 2 mm/min |
| 5 . | 10 K/min, DSC |
| 6 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer E70D | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| Wanthane® WHT-1585 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| BJB Polyurethane WC-782 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Eastar™ GN071, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Braskem PE ML3602U | Braskem | LLDPE | Braskem PE |