omay® V42B
| Category: | Film, PC , PC Film |
| Manufacturer: | Suzhou OMAY Optical Materials Co., Ltd |
| Trademark: | omay® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UwWUyP_omay-V42B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (150°C) | 0.50 to 0.70 | % | ASTM D1204 |
| Surface Tension | > 38 | mN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | 2B - B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 100 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 153 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 156 | °C | ISO 11357 |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM D5470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | VTM-2 VTM-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 A5RG7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 612 | Shandong PA612 |
| Silamid® CV20 | Roonamid a.s. | Nylon 6 | Silamid® |
| EnviroPCABS 5010IM | West Michigan Compounding | PC+ABS | EnviroPCABS |
| LONGLITE® PBT 2100-202B | CCP Group | PBT | LONGLITE® PBT |
| LEXAN™ EXL1890T resin | SABIC Innovative Plastics | PC | LEXAN™ |