LNP™ THERMOCOMP™ DX15354 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UwMvps_LNPTHERMOCOMPDX15354compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* DX15354 compound is a Polycarbonate (PC) compound with improved heat resistance performance, good plating, surface aesthetics and RF performance that makes it a good candidate for internal and external parts for Laser Direct Structuring (LDS) applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 63.0 | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2920 | MPa | ASTM D638 |
| -- | 2940 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 59.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 3 | 11 | % | ASTM D638 |
| Fracture | 11 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2890 | MPa | ASTM D790 |
| -- | 2880 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 111 | MPa | ASTM D790 |
| -- | 112 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 61 | J/m | ASTM D256 |
| 23°C 4 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2200 | J/m | ASTM D4812 |
| 23°C 5 | 180 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 168 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 155 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 2.95 | Internal method | |
| Dissipation Factor (1.10 GHz) | 6.0E-3 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 280 - 315 | °C | |
| Middle Temperature | 290 - 335 | °C | |
| Front Temperature | 300 - 345 | °C | |
| Nozzle Temperature | 295 - 340 | °C | |
| Processing (Melt) Temp | 300 - 345 | °C | |
| Mold Temperature | 95 - 130 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 90 | rpm | |
| Vent Depth | 0.025 - 0.080 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 80*10*3 |
| 5 . | 80*10*3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PVC BOTTLE GRADE K57 | Marco Polo International, Inc. | PVC, Rigid | MARPOL® PVC |
| WELLAMID Nylon 6000/50 CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Capilene® CE 50 E | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| NYLOY® MS-0200N-3-H | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| LNP™ LUBRICOMP™ IFL36 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |