LNP LUBRICOMP KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible. Also known as: LNP* LUBRICOMP* Compound 404 LE Product reorder name: KL004L |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.52 | g/cm³ | ASTM D792 |
| -- | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 3.4 | % | Internal method |
| Flow : 24 hours | 2.5 - 4.0 | % | ASTM D955 |
| Transverse flow | 2.5 | % | Internal method |
| Transverse flow : 24 hours | 2.0 - 3.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.5 | % | ISO 294-4 |
| Flow direction : 24 hours | 3.4 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2340 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield 2 | 47.9 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Fracture | 46.9 | MPa | ASTM D638 |
| Fracture 3 | 47.2 | MPa | ASTM D638 |
| Fracture | 47.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 11 | % | ASTM D638, ISO 527-2, ISO 527-2/5 |
| Yield 4 | 11 | % | ASTM D638 |
| Fracture | 22 | % | ASTM D638 |
| Fracture 5 | 22 | % | ASTM D638 |
| Fracture | 20 | % | ISO 527-2, ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2070 | MPa | ASTM D790 |
| -- | 2070 | MPa | ASTM D790 |
| -- | 2100 | MPa | ISO 178 |
| -- 7 | 2100 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 59.0 | MPa | ISO 178 |
| -- | 59.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.25 | ASTM D3702 Modified | |
| With Self-Static | 0.14 | ASTM D3702 Modified | |
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 8 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 670 | J/m | ASTM D4812 |
| 23°C 9 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.70 | J | ASTM D3763 |
| -- | 1.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 154 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 84.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 83.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 9000 | Colorite Polymers | PVC, Unspecified | Unichem |
| UNITRON® PPS | Nytef Plastics, Ltd. | PEEK | UNITRON® |
| CALP 4907G-3 | Lion Idemitsu Composites Co., Ltd. | PP, Unspecified | CALP |